20CrMo steel gears

  • 63 Views
  • 11-May-2024

can be a good machinability and cold plastic strain. KUNFENG as a supplier in china, more information about , please see the following:

Name:
Standard: GB / T 3077-1988
Corresponds to the standard: JIS G4053: 2003 ASTM A29M: 2005 ISO 683-18:1996

20CrMo gear steel chemical composition:

C

Si

Mn

S

P

Cr

Ni

Cu

Mo

0.17~0.24

0.17~0.37

0.40~0.70

≤0.035

≤0.035

0.80~1.10

≤0.030

≤0.030

0.15~0.25

20CrMo gear steel mechanical properties:
Tensile strength σb (MPa): ≥ 885 (90) Yield strength σs (MPa): ≥ 685 (70)
Elongation δ5 (%): ≥ 12 Reduction of area ψ (%): ≥ 50
Impact energy Akv (J): ≥ 78 Impact toughness values ​​αkv (J/cm2): ≥ 98 (10)
Hardness : ≤ 197HB Sample size: Sample size is 15mm rough

Heat treatment and microstructure specifications
Heat treatment specifications: quenching 880 ℃, water, oil cooling ; tempering 500 ℃, water, oil cooling .

20CrMo material belonging to a low-carbon alloy steel for carburizing ; treatment specifications : quenching 880 ℃, water, oil cooling ; tempering 500 ℃, water, oil cooling 20CrMo quenching (860-880 ℃ cold water or oil ) . plus low temperature (150 - 200 ℃) tempered , 20CrMo hardness HRC32-33.

Range gear steel 20CrMo characteristics and application: high hardenability , temper brittleness , very good weldability , cold cracking tendency to form small, can be a good machinability and cold plastic strain . Usually in the quenched state or carburizing used for the manufacture of infiltration in non-corrosive media and working temperatures below 250 ℃, pressure pipe and various fasteners containing nitrogen and hydrogen mixture of media work , more advanced carbon parts, such as gears , shafts , etc.

Related Post

201 Stainless Steel Flat Bar

Chemical Composition

GB/T 9711-2011 L290R/X42R PSL2 LSAW pipeline

GB/T9711-2011 L290R/X42R PSL2 LSAW pipeline is an industrial steel pipe,L290R/X42R PSL2 LSAW pipeline is mainly used in the field of construction, shipbuilding, petrochemical, hydropower industry, can accept chemical composition analysis, mechanical properties, technical performance, size inspection, non-destructive testing, hydraulic test, SR1 electromagnetic inspection.

RMRS FH40 shipbuilding steel plate

The RMRS FH40 grade steel plates have yield strength of 56,500 psi (390 MPa), and ultimate tensile strength of 74,000 - 94,500 psi (510-650 MPa). RMRS FH40 steel can achieve the impact toughness at Celsius degree -60°. All the RMRS FH40 shipbuilding Steel

A204 GR.C steel works/steel structures/steel machining parts

ASTM A 204Gr.C steel has the proper tensile strength, good toughness, low effectiveness of the tendency, plasticity, processing property, be rolled into steel plates, shaped steel and profile steel.