KR FH40 shipbuilding steel plate

  • 34 Views
  • 10-May-2024

The KR EH40 grade steel plates have yield strength of 56,500 psi (390 MPa), and ultimate tensile strength of 74,000 - 94,500 psi (510-650 MPa).KR FH40 shipbuilding steel plate is a kind of hot rolled high tensile strength steel. Higher-strength KR shipbuilding steel comes in 12 grades of 3 strengths, KR FH40 shipbuilding steel plates is one of the grades.

The application of KR FH40 shipbuilding steel plate

KR EH40 Shipbuilding steel plates are suitable for container and bulk cargo vessels as well as cruise ships, ferries and yachts.

KR FH40 shipbuilding steel plate Chemical Composition

Grade

C %

Si %

Mn %

P %

S %

V %

AL %

Cr %

KR EH40

0.180

0.1-0.5

0.90-1.6

0.035

0.035

0.05-0.10

0.015

0.200

Cu %

Mo %

Nb %

Ni %

Ti %

 

 

 

0.350

0.080

0.02-0.05

0.400

0.020

 

 

 

KR FH40 shipbuilding steel plate Mechanical Properties

Grade

Thickness(mm)

MinYield(Mpa)

Tensile(Mpa)

Elongation (%)

Min Impact Energy

KR EH40

8mm-50mm

Min 390Mpa

510-650Mpa

20%

-40

34J

51mm-70mm

Min390Mpa

510-650Mpa

20%

-40

41J

71mm-100mm

Min 390Mpa

510-650Mpa

20%

-40

50J

The min impact energy is longitudinal energy

The rolling size of KR FH40 shipbuilding steel plate

Thickness

3-150mm

Width

1220-4200mm

Length

5000-18000mm

Notes: coil thickness ≤ 25mm
All of KR FH40 shipbuilding steel plates have been engineered to be optimal long-lived shipbuilding steels.welcome to contact KUNFENG if you are loooking for the best suppliers of KR FH40 shipbuilding steel plates. We will try our best to reply you at the first time.KR FH40 shipbuilding steel plate’s quality can be guaranteed.

Related Post

GL DH40 shipbuilding steel plate

GL DH40 shipbuilding steel plate are mainly used to build vessels which are sailing in low temperature oceans.When rolling GL DH40 shipbuilding steel plate, TMCP or Normalized shall be done for heat treatment,and low temperature impacting test have to be

Custom Non Standard Parts Supplier

Non-standard parts are unique and cannot be substituted with any other parts due to their customized production process.

PYD-1600Z cone crusher crushing wall price

The quality of material we used for components and reasonable design of construction contributes to its longer running performance and even granularity of the crushed product in addition to reducing to circulation load.

GB/T13793-2008 Grade 10 welded steel pipe

GB/T13793-2008 Grade 10 welded steel pipe for oil and natural gas. GB/T13793 Grade 10 steel pipe is made by resistance welding or cold and hot processing after hot rolling or cold rolling. It adopts the flattening test, bending test, flaring test, hydraulic test, surface test. Galvanized, good yield strength and tensile strength.