SAE J403 SAE1008 steel work / steel structure / steel machining parts

  • 75 Views
  • 10-May-2024

SAE1008 steel contains very low carbon so it is called low carbon steel. It is suitable for the stamping and cold forming.

We keep more than 1000 ton SAE1008 steel stock. Based on the stock, we can produce many specifications of SAE1008 steel work / steel structure / steel machining parts based on the customer's requirement.

The following datasheet will provide more details about SAE 1008 steel work .

SAE 1008 steel work chemical composition

Element

Content (%)

Iron, Fe

99.31-99.7 %

Manganese, Mn

0.30-0.50 %

Carbon, C

0.10 %

Sulfur, S

0.050 %

Phosphorous, P

0.040 %

SAE 1008 steel structure physical properties

Properties

Metric

Imperial

Density (composition 0.06% C, 0.38% Mn, 0.01% Si, annealed at 925°C)

7.872 g/cm3

0.2844 lb/in³

SAE 1008 steel apare parts mechanical properties

Properties

Metric

Imperial

Tensile strength

340 MPa

49300 psi

Yield strength (depending on temper)

285 MPa

41300 psi

Elastic modulus

190-210 Gpa

27557-30458 ksi

Bulk modulus (typical for steel)

200 GPa

29000 ksi

Shear modulus (typical for steel)

80.0 GPa

11600 ksi

Poisson’s ratio

0.27-0.30

0.27-0.30

Elongation at break (in 50 mm)

20%

20%

Reduction of area

45%

45%

Hardness, Brinell

95

95

Hardness, Knoop (converted from Brinell hardness)

113

113

Hardness, Rockwell B (converted from Brinell hardness)

55

55

Hardness, Vickers (converted from Brinell hardness)

98

98

Machinability (based on AISI 1212 steel as 100 machinability) The machinability of group I bar, rod, and wire products can be improved by cold drawing)

55

55

SAE 1008 steel structure thermal properties are tabulated below

Properties

Metric

Imperial

Thermal expansion co-efficient (@0.000-100°C/32-212°F)

12.6 µm/m°C

7 µin/in°F

Thermal conductivity (composition of 0.06% C, 0.4% Mn; 0°C )

65.2 W/mK

452 BTU in/hr.ft².°F

SAE 1008 steel work Applications

AISI 1008 low carbon steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.

SAE 1008 steel machining parts Production technology

Drilling, cutting, bending, welding, groove, correction, edge processing, spraying assembly etc.

Shanghai KUNFENG has been engaged in the steel work industry for many years. We have much experience in fabricating the SAE 1008 steel work / steel structure / steel machining parts. If you have the demand for this products, please contact us.

Related Post

20CrMo hot rolled round bars and forged round bars

20CrMo round bar is the alloy structural round bar under the standard of GB/T 3077-1988.20 CrMo hot rolled round bars and forged round bars has high harden ability and no temper brittleness.

S45C hot rolled round bars and forged round bars

S45C round bar is a kind of high carbon round bar which based on the standard of JIS G 4051-2009 . S45C round bars have excellent weldability and machinability, and they can be subjected to various heat treatments.

ASTM A204 Grade (Gr) B Pressure vessel and Boiler steel plate

KUNFENG is the supplier of ASTM A204 Grade (Gr) B Pressure vessel and Boiler steel plate.ASTM A204 Grade B pressure vessel steel plate is a kind of Mo-alloy steel material used to fabric high temperature pressure vessels.

API5L X80 PSL2 LSAW steel pipeline

API5L X80 PSL2 LSAW steel pipeline is a variant of API 5L. API standards for American Petroleum Institute. For API 5L X80 PSL2 LSAW Steel Pipes, the wall thickness and other requirements are different than other API 5L variants