42CrMo4 Alloy Steel

42CrMo4 Alloy Steel

42CrMo4 steel is a kind of alloy structural steel. 42CrMo4 steel is generally intended for fabrication of quenched and tempered, flame or induction hardened machine parts.

Category: Alloy Steel
Hits: 394
Updatetime: 27-Jul-2023

Grade: 42CrMo4 Steel 

Type : steel plate, round bar,flat bar 

Standard: EN 10083-3 

Steel Plate Thickness:  

Thickness: 3mm--300mm

Width: 1500mm--4050mm 

Length: 3000mm to 27000mm 

Place of Origin:  China

Brand Name:  KUNFENG

42CrMo4 Application:

42CrMo4 steel is generally intended for fabrication of quenched and tempered, flame or induction hardened machine parts.

42CrMo4 Steel Introduction 

42CrMo4 steel is  is characterized by good hardness and high strength, hardenability, deformation is little when be quenched, high creep and rupture strength at high temperature, generally intended for fabrication of quenched and tempered, flame or induction hardened machine parts.

42CrMo4 Steel Delivery state

42CrMo4 Steel Material should be delivered at Q+T (quenched and tempered) conditions.

42CrMo4 Steel Application

42CrMo4 steel is generally intended for fabrication of quenched and tempered, flame or induction hardened machine parts.

42CrMo4 Steel Chemical Composition Analysis% 

C Si Mn P S Cr Mo

0.38- 0.45 max 0.40 0.60-0.90 Max  0.025 Max 0.035 0.90- 1.20 0.15 – 0.30

42CrMo4 Steel Mechanical Properties

Grade 42CrMo4 Mechanical Property

Thickness Yield Tensile Elongation

42CrMo4 mm Min Mpa Mpa Min  %

3<t≦8 900 1100-1300 10

8<t≦20 750 1000-1200 11

20<t≦60 650 900-1100 12

60<t≦100 550 800-950 13

100<t≦160 500 750-900 14

42CrMo4 Steel Packing

42CrMo4 Steel Packing is normally wrapped by plastic film and waterproof paper, and then fastened on wooden pallet or as you request.


Related Post

P20+Ni Steel Plate

P20+Ni steel has good mechanical property and quenching, make surface have equal hardness after deal with it. Nice polishing and low roughness. Normally make the heat-treatment to harden condition before used, it can be used directly after the mould machined.

4140, 42CrMo4, 1.7225 alloy steel

SAE 4140 steel is widely used in many industrial fields for its strength and versatility, and therefore is important to know about if you are considering using it in your facility. Here is an outline of its key characteristics and most common applications. 4140 is low alloy steel with chromium an

ASTM A 204 gr.C steel,A 204 gr.C Manufacturer

Product name:ASTM A 204 Gr.C carbon steel plate Standard: GB JIS ASTM AISI DIN ect Material:ASTM A36 A285 A 238 A516, A572 A387 A 204 ,16Mn,TP 201 304 316 ect

A 387 gr.12 Chemical composition,A 387 gr.12 Mechanical properties

As a quality chrome moly steel, A387 Grade 12 Class 2 is used in a variety of industries and is highly effective, particularly in the oil, gas and chemical industry, where liquids and gases are often stored at high temperature (see pressure vessels). The higher levels of chromium also provid