SAE J403 SAE1010 steel work / steel structure / steel machining parts

  • 68 Views
  • 10-May-2024

SAE J403 SAE 1010 steel as stamping and cold forming steels. This steel has relatively low strength but it can be quenched and tempered to increase strength.

SAE1010 steel work / steel structure / steel machining parts is made from SAE 1010 steel, which widely used in Automobile components, including auto bodies, fenders, pans, transmission covers and so on.

For more information about SAE1010 steel structure , please see the following :

SAE 1010 steel work Chemical analysis -% by mass*

Chemical elements

C

Si 
max

Mn
max

P
max.

S
max.

SAE 1010 steel work

0.12

--

0.60

0.045

0.045

SAE 1010 steel structure Mechanical properties

Annealing hardness
HBS

Cold pull hardness
HBS

Preheating temperature

Quenching temperature

Holding time
min

Hardening medium

Temper temperature

After tempering hardness
≥HRC

salt-bath furnace

controlled atmoSPHEre furnace

235

262

788

1191

1204

5~15

air cooling

522

60

SAE 1010 steel machining parts Technological properties

Steel plate/Sheet
thickness / mm

σb
MPa

σs
≥/MPa

δ
Samples from the standard for 50 mm (2 in) 

180 ° of cold bending test

longitudinal

horizontal

Hot-rolled/Cold rolling:5 - 150

520

415

16~18

2a

3.5a

we have Professional SAE1010 steel work manufacturing equipments, such as : Plasma Cutting Machine, Flame Cutting Machine, Horizontal automatic welding machine, CNC Cutting Machine, CNC drilling machine etc. Based on these equipments, we can offer SAE1010 steel Drilling, cutting, bending, welding, groove, correction, edge processing, spraying assembly service.

SAE1010 steel structure Heat treatment technology

Annealing, quenching, tempering, quenching and tempering

Shanghai KUNFENG has been engaged in the steel work industry for many years. We have much experience in fabricating the SAE 1008 steel work / steel structure / steel machining parts. If you have the demand for this products, please contact us.

 

Related Post

Sand maker(Sand making machine) spare parts, Segregation cone

The segregation cone of sand making machine is installed at the bottom of upper endcover and the lower part of the feeding tube.

310S Stainless Steel Tube

Chemical Composition

904L stainless steel round bar supplier

904L stainless steel round bar 1.4539 is a high-alloy austenitic stainless steel with low carbon content. 904L has good resistance to general corrosion, particularly in sulfuric and phosphoric conditions.

SEW087 WTSt 37-3,WTSt 37-3 steel,WTSt 37-3 grade,WTSt 37-3 steel grade,WTSt 37-3 steel plate,WTSt 37

WTSt 37-3 steel plate price and WTSt 37-3 steel plate price specification can be provided by KUNFENG ,if you need WTSt 37-3 steel plate,please contact us.