API 2W Gr.50/Gr.60 steel work / steel structure / steel machining parts

  • 88 Views
  • 10-May-2024

API 2W Gr.50/Gr.60 steel work / steel structure / steelmachining parts

API 2W Gr.50/Gr.60 steel work/steelstructure/steelmachiningparts are mainly used in the managed node,with a plus Zhu board structure and other cross site,In these parts of the steel sheet in the thickness direction (Z-direction) shall be subjected to tensile loading.

API 2W Gr.50/Gr.60 steel specification covers high strength steel plates, use in welded construction of offshore structures,in selected critical portions which must resist impact,
plastic fatigue loading,and lamellar tearing,grade 50 up to 6in.thick. (150mm),grade 60 up to 4in.(100mm).

API 2W Gr.50/Gr.60 steel chemical composition

Element

Gr.50

Gr.60

C max

0.16

0.16

Mn under 1.5in.40mm

1.15-1.60

1.15-1.60

Mn over 1.5n.40mm

1.15-1.60

1.15-1.60

P max

0.030

0.030

S max

0.010

0.010

Si

0.05-0.50

0.05-0.50

Ni max

0.75

1.0

Cr max

0.25

0.25

Mo max

0.08

0.15

Cu max

0.35

0.35

Ti N≦0.005

0.003-0.02

0.003-0.02

Ti N>0.005

0.007-0.02

0.007-0.02

Nb max

0.03

0.03

N max

0.012

0.012

B max

0.0005

0.0005

API 2W Gr.50/Gr.60 steel mechanical properties

Property

Gr.50

Gr.60

yield strength ksi(mpa)

 

 

t≤1in.(25mm)

50-75(345-517)

60-90(414-621)

t>1in.(25mm)

50-70(345-483)

60-85(414-586)

Tensile Strength,ksi(mpa),min

65(448)

75(517)

2in.(50mm)elongation,min,%

23

22

8in.(200mm)elongation,min,%

18

16

API 2W Gr.50/Gr.60 steel heat treatment

Due to the inherent characteristics of the TMCP method, plates manufactured to this spec cannot be formed or postweld heat treated at temperatures above 1100°F (595°C) without some risk of sustaining irreversible and significant losses in strength and toughness. If warm-forming is to be required during subsequent fabrication, the tensile and notch toughness properties of the finished component shall be verified and the properties shall conform to the requirements of this specification. The procedure for verification shall be subject to mutual agreement. The plates may be post-weld heat treated at elevated temperatures not exceeding 1100°F (595°C) providing test coupons are subjected to a thermal cycle to stimulate such fabrication operations, as described in Supplementary Requirement S9. Verification or simulation is not necessary for heating at temperatures not exceeding 400°F (205°C). 

API 2W Gr.50/Gr.60 steel work/steelstructure/steel machiningparts testing equipment

calipers,pressure sensors,magnetic particle inspection machine,digital ultrasonic flaw detector,hydraulic universal testing machine,digital thickness gauge etc.

KUNFENG have been playing vital supplier role in the full spectrum of industries ranging from oil and gas,power plant,cement plant,shipbuilding,bridge,building,crane building etc. We not only can supply API 2W Gr.50/Gr.60 steel work/steelstructure/steelmachiningparts,
also can provide Heat reatment,Test,Galvanization,pre-treatment,Cutting etc service,
If you need API 2W Gr.50/Gr.60 steel work/steelstructure/steelmachiningparts,contact us!

Related Post

EN10025 S420J0 carbon and low alloy steel plate for sale

With the continuous development of the international steel trade, many customers began to look for EN10025 S420J0 carbon and low alloy steel plate suppliers in China. now,many factory began to product other country’s standard.

310S Stainless Steel Bar

Chemical Composition

Concave Bowl Liner

We supply high qualified concave in high Cr, Mo, alloy steel for Cone Crusher. Mining equipment spare parts,primary crushing replacement parts,crushing machine spare parts,stone crusher wear parts,quarry equipment spare parts.

1340 hot rolled round bars and forged round bars

1340 round bars has high Strength, plasticity and wear resistance, but the cold deformation plasticity is not high, weldability is poor.