4130 alloy steel

4130 alloy steel

AISI 4130 steel can be easily machined using conventional methods. However, machining becomes difficult when the hardness of the steel is increased. Forming of AISI 4130 steel can be performed in the annealed condition. 4130 steel have a high modulus of elasticity which means they can endure larg

Category: Steel Materials
Hits: 726
Updatetime: 27-Jul-2023

AISI 4130 steel can be easily machined using conventional methods. However, machining becomes difficult when the hardness of the steel is increased. 

Forming of AISI 4130 steel can be performed in the annealed condition. 4130 steel have a high modulus of elasticity which means they can endure large amounts of strain and still return to their original shape. 

4130 steel properties on being subjected to machining or fabrication processes such as milling and welding can manufacture many products. It is currently an important part of the automotive industry and is used to manufacture gears, drill bits, cutting tools, etc.

Related Post

ASTM A 387 gr.2 steel,A 387 gr.2 Manufacturer

Steel Plate,ASTM,ASME,(S)A387 Grade 2, (S)A387 Grade 12, (S)A387 Grade 11,(S)A387 Grade 22,(S)A387 Grade 22L,(S)A387 Grade 21,(S)A387 Grade 21L,(S)A387 Grade 5,(S)A387 Grade 9,(S)A387 Grade 91,(S)A387 Grade 911,Pressure Vessel Plates, Alloy Steel, Chromium-Molybdenum,(S)A 387/(S)A 387M standard.

EN10025-6: S960QL1, S960QL1 steel, S960QL1 steel plate

S960QL1 is a hot rolled structural steel, with high yield strength, delivered in the quenched and tempered condition.

A202 gr.A Chemical composition,A202 gr.A Mechanical properties

A202 gr.A Chemical composition,A202 gr.A Mechanical properties: KUNFENG steel is specialized in supplying ASTM A202 steel plate in A202 grade A. For more information of A202 grade A steel plates.

201 stainless steel

ASTM A959 201 stainless steel is an austenitic chromium-nickel-manganese stainless steel that was developed originally to conserve nickel. ASTM A959 201 stainless steel is nonmagnetic in the annealed condition, but becomes slightly magnetic when cold worked. Toughness at low temperature is excell